Kimfill presents different grades of reinforced polyamide 6 and 66 (Nylon 6 and 66) which are used in various industries with different colors and applications.

Technical information of kimfill (based on PA6) is outlined in following table:

Grade Application/Specification Mechanical Properties of PA6 Reinforced Compounds
Test Filler Content Density Tensile Modulus Tensile Strength Elongation (@ Break) Unnotched Charpy Impact Strength Notched Charpy Impact Strength
Test Standard ISO 3451 ISO 1183 ISO 527 ISO 179
Color Base Polymer Filler Type % g/cm3 MPa MPa % KJ/m2
Kimfill 4616 Home Appliances and  Automotive, High Impact Resistance, Excellent
Processing 
Black PA6 Glass Fiber 15±2 1.24 5000 110±5 (a) 5 40-45
Kimfill 4628 Home Appliances , Automotive Components, Electrical & Electronic
Parts, Economical Grade
Black PA6 30±2 1.36 6300 120±5 (a) 4 45-50
Kimfill 4630 Home Appliances, Internal & External Automotive Parts, Electrical &
Electronic Parts , Excellent Tensile Strength, High Impact Resistance, 
Excellent  Processing
Black PA6 30±2 1.36 8500 160±5 (a) 5 80-85 13
Kimfill 4631 Home Appliances, Internal & External Automotive Parts, Electrical &
Electronic Parts,  Excellent Tensile Strength, High Impact Resistance, 
Excellent  Processing
Natural PA6 30±2 1.36 8500 160±5 (a) 5 80-90 13.5
Kimfill 4632 Internal & External Automotive Parts,  Appropriate Economical
and Mechanical Features
Black PA6 30±2 1.36 8000 145±5 (a) 4 70-75 11
Kimfill 4633 Home Appliances, Internal & External Automotive Parts, Electrical &
Electronic Parts,  Excellent Tensile Strength, High Impact Resistance, 
Excellent  Processing
Natural PA6 30±2 1.36 8800 165±5 (a) 5 90-95 14
Kimfill 4636 Automotive Parts(Manifold),  High Thermal Stability, Excellent
Mechanical
Properties, High Abrasion Resistance
Black PA6 35±2 1.37 9000 170±5 (a) 4 80-85 13
Kimfill 4638 Automotive Parts, Rail way Parts, High Thermal Stability, Excellent
Mechanical
Properties, High Abrasion Resistance
Black PA6 40±2 1.45 11000 185±5 (a) 4 80-85 13
Kimfill 4642 Home Appliances , Automotive Components, Electrical & Electronic
Parts, Economical Grade
Black PA6 32±2 1.37 6500 130±5 (a) 4 45-50
Kimfill 4644 Home Appliances , Automotive Components, Electrical & Electronic
Parts, Economical Grade
Black PA6 40±2 1.45 8000 150±5 (a) 4 50-60
Kimfill 4650 Electrical Parts, Special Parts, Very High Mechanical Properties Black PA6 50±2 1.56 13000 185±5 (a) 3.5 75-80 13

(a)=5mm/min (b)=50mm/min

Technical information of kimfill (based on PA66) is outlined in following tables:

Grade Application/Specification Mechanical Properties of PA66 Reinforced Compounds
Test Filler Content Density Tensile Modulus Tensile Strength Elongation (@ Break) Unnotched Charpy Impact Strength Notched Charpy Impact Strength
Test Standard ISO 3451 ISO 1183 ISO 527 ISO 179
Color Base Polymer Filler Type % g/cm3 MPa MPa % KJ/m2
Kimfill 4520 Home Appliances , Electrical and Electronic Parts and Automotive Under
Hood, Excellent Processing, Good Mechanical Properties
Black PA66 Glass Fiber 20±1 1.28 7000 135±5 (a) 5 50-60
Kimfill 4526 Home Appliances , Electrical and Electronic Parts and Automotive Under
Hood, Good Mechanical Properties
Black PA66 25±2 1.29 7500 145±5 (a) 5 55-63
Kimfill 4530 Home Appliances , Electrical and Electronic Parts and Automotive Under
Hood,  Excellent Mechanical  Properties and Thermal Stability
Black PA66 30±1 1.33 10000 170±5 (a) 4 70-80
Kimfill 4531 Home Appliances , Electrical and Electronic Parts and Automotive Under
Hood,  Excellent Mechanical Properties  and Thermal Stability
Natural PA66 30±1 1.33 10000 170±5 (a) 4 75-80
Kimfill 4532 Automotive Parts, Electrical and Electronic Parts,  Appropriate
Economical and Mechanical Features
Black PA66 30±3 1.33 8000 140±5 (a) 4 60-65
Kimfill 4534 Home Appliances , Electrical, Electronic and Automotive Parts, 
Economical Grade
Black PA66 32±3 1.34 7000 130±5 (a) 4 50-60
Kimfill 4540  Electrical, Electronic and Automotive Parts, , Good Mechanical
Properties, Economical Grade
Black Hybrid 35±3 1.38 7000 145±5 (a) 3.5 50-60
Kimfill 4549 Special Parts, ,  Excellent Mechanical  Properties and Thermal
Stability
Natural PA66 50±2 1.55 13500 210±5 (a) 3 85-95

(a)=5mm/min (b)=50mm/min